Welding vs. Soldering vs. Brazing–What’s the difference?

welder using torch

TWS is a Great Training Option for Everyone

Learn more about how we can prepare you to advance your career.

Welding, soldering, and brazing are all techniques to join two or more pieces of metal and in some cases, other materials. They are also techniques for filling gaps in metal parts. So, how do you determine which technique to use? That decision depends on material, desired strength, and application.



The purpose of welding is to create a very strong bond between two pieces of metal that can withstand all kinds of stresses and strains, such as a car body or aircraft fuselage. What goes into welding?

  • Two metals must be similar: To weld two metals together, they must be similar. For example, you can’t weld copper to steel.
  • High temperature: The temperature needed to weld two metals together must be very high so they melt and join.
  • Filler materials: You often use a filler material in welding which is an extra piece of metal that seals any gaps.
  • Strength: If the welding job was properly done, the weld should be as strong as the surrounding, “unwelded” metal. Too much heat, for instance, can change the metal’s characteristics and weaken the weld.
  • Different welding techniques: There are various welding techniques, depending on what metal you work on. In a welding program, you can learn which technique to use with what kind of metal. Different welding techniques have different heat sources, like oxyacetylene gas, electrodes, lasers, or ultrasonics.



Soldering may look similar to welding, but it has quite a different purpose. A solder is rather soft and normally comes in tubes and reels. A solder is used in electronic devices where it allows the components to connect with each other electronically. What goes into soldering?

Have You Considered a Career in the Skilled Trades?

Fill out the form to recieve a no obligation info packet.

You are giving your express written consent for Tulsa Welding School to contact you regarding our educational programs and services using email, telephone or text including our use of automated technology for calls or texts to any wireless number you provide. This consent is not required to purchase goods or services and you may always call us directly at (855) 237-7711.

+ Read More
  • Low temperature: Unlike welding, soldering uses a low temperature to join metals.
  • Filler materials: Soldering is done with fillers that melt at below 840 °F (450°C).
  • Different metals can be soldered: Metals that can be soldered include gold, silver, copper, brass, and iron. The bond created when the melted soldered material solidifies.
  • Not as strong as welding or brazing. A soldered bond is not as strong as a welded or brazed one because it is not a mechanical connection. If soldering wasn’t done properly, the pieces won’t conduct electricity properly.
  • Flux is used: Just as in welding and brazing, flux is used to clean metal surfaces, so that the solder can flow over the pieces that will be joined.



Brazing is akin to soldering in that it also uses filler for joining two metals, albeit a high-temperature one. Similar to welding, brazing creates a mechanical connection between to metal parts. What goes into brazing?

  • Joining metals by melting filler: Brazing consists of heating and melting a filler alloy. Once the filler solidifies, the metal pieces are joined.
  • Filler materials: The filler alloy must have a lower melting temperature than the metal pieces.
  • Dissimilar metals: Brazing allows for the joining of different metals like aluminum, silver, copper, gold, and nickel.
  • Flux is often used: Liquid flux material promotes wetting of the metal parts, which lets the filler flow over them, so they can be joined more easily.
  • Strength: While properly brazed joins can be stronger than the individual pieces, they are not as strong as welded joints. 1 2

Welding, soldering, and brazing are used for different jobs. Depending on the work you do, you have to consider factors like metal type, desired strength, and ultimate purpose to determine how to join two or more pieces of metal. With sufficient practice, you can master each technique well.